         Index            Ts             t             f             F             x         Phase            F0            x0            Tr            E'            E"            E*     tan_delta            D'            D"            D*
           [#]          [C]           [s]          [Hz]           [N]          [um]         [rad]           [N]          [um]          [C]         [MPa]         [MPa]         [MPa]            []       [1/MPa]       [1/MPa]       [1/MPa]
             0  2.48786e+001  2.00000e+001  9.99999e-001  9.77484e-002  3.11614e-001 -9.52046e-003  1.52005e-001 -5.30205e+001  2.83333e+001  2.70316e+003 -2.73321e+001  2.70329e+003 -1.01112e-002  3.69900e-004 -3.74013e-006  3.69919e-004
             1  2.69695e+001  2.90000e+001  9.99999e-001  9.58552e-002  3.22084e-001  6.66913e-003  1.51573e-001 -5.15613e+001  2.98333e+001  2.56023e+003  1.69489e+001  2.56028e+003  6.62008e-003  3.90573e-004  2.58563e-006  3.90582e-004
             2  3.07569e+001  4.10000e+001  9.99999e-001  9.98803e-002  3.42119e-001  1.66714e-002  1.52145e-001 -5.06487e+001  3.18333e+001  2.50965e+003  4.25058e+001  2.51001e+003  1.69369e-002  3.98348e-004  6.74678e-006  3.98405e-004
             3  3.44265e+001  5.00000e+001  9.99999e-001  1.01829e-001  3.55610e-001  1.20771e-002  1.51953e-001 -4.97831e+001  3.33333e+001  2.46024e+003  2.99867e+001  2.46042e+003  1.21885e-002  4.06405e-004  4.95348e-006  4.06435e-004
             4  3.70235e+001  5.90000e+001  9.99999e-001  9.87932e-002  3.49637e-001  1.39389e-002  1.51304e-001 -4.91479e+001  3.48333e+001  2.42659e+003  3.42217e+001  2.42684e+003  1.41028e-002  4.12018e-004  5.81059e-006  4.12059e-004
tensionclass, 31.03.2014 17:12:33